Products > hard-face material > tungsten carbide copper welding rod > 6% Co Hardness 92hra Od350*ID80*3.0mm Tungsten Carbide Circular Cutters

Product name : 6% Co Hardness 92hra Od350*ID80*3.0mm Tungsten Carbide Circular Cutters

Product No. : OD350*ID80*3.0mm

[Next Product]→

Online Inquiry Email Us

Details:

6% Co Hardness 92hra Od350*ID80*3.0mm Tungsten Carbide Circular Cutters
6% Co Hardness 92hra Od350*ID80*3.0mm Tungsten Carbide Circular Cutters

tungsten carbide disc cutter usually is machined into all kinds cutter with tooth,tungsten carbide
lead wire cutter with excellent hardness and abrasive resistance .

1. the thickness can reach 0.5mm for unground disc cutter.

2. Sintere by vacuum sintering furnace and HIP machine with excellent specifications without any hole.

3. can suply unground cutter or process according drawing,such as grinding face,outdiameter,inner-
hole,punching,making slotting,blade or teeth ect.

4. Suitable for machining hardened steel, alloy steel, cast iron, non-ferrous metal, stainless steel, high
manganese steel, plywood, PCB, PVC, electronic board.

Grade specifications

Grade	Density g/cm3	T.R.S Mpa	Hardness HRA	Performance & application recommended	ISO code
YG6X	14.9	1850	92	Fine grain alloy, good wear resistance. Semifinishing of chilled cast iron, non-ferrors metals alloys, semi-finishing and finishing of hardened steel, alloy steel.	K10
YG6	14.9	2450	90.5	High wear resistance, bending strength, suitable for electronic industry with the disc cutting knife.	K10
YG8	14.8	2450	90.5	High strength ,impact and shock resistance higher than YG6X,,but wear resistance and cutting speed comparatively lower.Roughing of cast irons,non-ferrors metals and their alloys as well as non metallic materials at low cutting speed	K20
YG10X	14.7	2320	89.5	High strength in use, impact and shock resistance higher than YG6, but wear resistance and cutting speed comparatively lower. Roughing of cast irons, non-ferrors metals and their alloys as well as	K40
YS2T	14.5	2200	91	Fine grain alloy, good wear resistance. Used for processing hard wood,veneer board,PCB,PVC and metals.	M10

Sizes choosing:

TYPE	OD(mm)	ID (mm)	S (mm)	TYPE	OD(mm)	ID (mm)	S (mm)
Φ12×Φ6×S	12	6	0.6-4.5	Φ60×Φ19×S	60	19	0.8-7.0
Φ13×Φ6×S	13	6	0.6-4.5	Φ63×Φ17×S	63	17	0.8-7.0
Φ16×Φ6×S	16	6	0.6-4.5	Φ70×Φ22×S	70	22	0.8-7.0
Φ22×Φ10×S	22	10	0.6-4.5	Φ75×Φ22×S	75	22	0.8-7.0
Φ25×Φ12×S	25	12	0.6-5.5	Φ80×Φ22×S	80	22	0.8-7.0
Φ32×Φ10×S	32	10	0.8-5.5	Φ83×Φ21×S	83	21	0.8-7.0
Φ40×Φ10×S	40	10	0.8-6.0	Φ86.5×Φ21.5×S	86.5	21.5	1.0-7.0
Φ45×Φ13×S	45	13	0.8-6.0	Φ90×Φ22×S	90	22	1.0-7.0
Φ53×Φ13×S	53	13	0.8-6.0	Φ100×Φ22×S	100	22	1.0-7.0
Φ52×Φ24.5×S	52	24.5	0.8-6.0	Φ125×Φ22×S	125	22	1.0-7.0
Φ53×Φ24.5×S	53	24.5	0.8-6.0	Φ200×Φ70×S	200	70	3.0-4.5
Φ55×Φ16×S	55	16	0.8-6.0	Φ250×Φ70×S	250	70	3.0-4.5
Φ58×Φ22×S	58	22	0.8-6.0	Φ310~350×Φ208×S	310~350	80~208	2.0-7.0